Alloy
No. Casting methode Tensil strength 0,2 % Yield point Elongation Brinell hardness
EN 1982
and Alloy describtion Rm Rp0,2 A5 HB
Min. N/mm2 Min. N/mm2 Min. % Min.
Cu Sn5 Zn5 Pb5-C
CC491K
-GS
Sand cast Rg5
200 90 13 60
Cu Sn5 Zn5 Pb2-C
CC499K
-GS
Sand cast Rg5 (Pb max. 3%)
200 90 13 60
Cu Sn7 Zn4 Pb7-C
CC493K
-GS
Sand cast Rg7
230 120 15 60
 
-GC
Continuous cast Rg7
260 120 12 70
   
-GZ
Centrifugal cast Rg7
260 120 12 70
Cu Sn9 Pb2 Zn4-C
No standard
-GS
Sand cast Rg9
230 110 12 75
Top
Alloy
No. Casting methode Tensil strength 0,2 % Yield point Elongation Brinell hardness
EN 1982 and Alloy describtion Rm Rp0,2 A5 HB
    Min. N/mm2 Min. N/mm2 Min. % Min.
Cu Sn10-C
CC480K
-GS
Sand cast 90/10 bronze
250 130 18 70
Cu Sn12-C
CC483K
-GS
Sand cast 88/12 bronze
260 140 7 80
 
-GC
Continuous cast 88/12 bronze
300 150 6 90
   
-GZ
Centrifugal cast 88/12 bronze
280 150 5 90
Cu Sn12 Ni2-C
CC484K
-GS
Sand cast 88/12Ni bronze
280 160 12 85
 
-GC
Continuous cast 88/12Ni bronze
300 180 8 95
   
-GZ
Centrifugal cast 88/12Ni bronze
300 180 10 95
Top
Alloy
No. Casting methode Tensil strength 0,2 % Yield point Elongation Brinell hardness
EN 1982 and Alloy describtion Rm Rp0,2 A5 HB
Min. N/mm2 Min. N/mm2 Min. % Min.
Cu Sn10 Pb10-C
CC495K
-GS
Sand cast Pb10Bz
180 80 8 60
 
-GZ
Centrifugal cast Pb10Bz
220 110 6 70
   
-GC
Continuous cast Pb10Bz
220 110 8 70
Cu Sn7 Pb15-C
CC496K
-GS
Sand cast Pb15Bz
170 80 8 60
 
-GZ
Centrifugal cast Pb15Bz
200 90 7 65
   
-GC
Continuous cast Pb15Bz
200 90 8 65
Top
Alloy
No. Casting methode Tensil strength 0,2 % Yield point Elongation Brinell hardness
  and Alloy describtion Rm Rp0,2 A5 HB
  Min. N/mm2 Min. N/mm2 Min. % Min.
Cu Zn21 Si3-C
No standard
-GS
Sand cast ECOCAST
700 450 25 190
Cu Zn40-C
No standard
-GS
Sand cast BRASS
Ca. 300 Ca. 90 Ca. 13-40 Ca. 60
Top
Alloy
No. Casting methode Tensil strength 0,2 % Yield point Elongation Brinell hardness
EN 1982
and Alloy describtion Rm Rp0,2 A5 HB
    Min. N/mm2 Min. N/mm2 Min. % Min.
Cu Al10 Fe5 Ni5-C
CC333G
-GS
Sand cast AluBz
600 250 13 140
 
-GZ
Centrifugal cast AluBz
650 280 13 150
 
-GC
Continuous cast AluBz
650 280 13 150
Cu Al11 Fe6 Ni6-C
CC334G
-GS
Sand cast AluBz
680 320 5 170
 
-GZ
Centrifugal cast AluBz
750 380 5 185
Cu Al10 Ni5 Fe4, R680S
CW307G
h11
Drawn bars
680 Ca. 480 10 170
Cu Al10 Ni5 Fe4, R740S
CW307G
h11
Drawn bars
740 Ca. 530 8 180
Cu Al10 Ni5 Fe4
CW307G
M
Bars Tolerance Klasse A Ca. 640 Ca. 270 Ca. 15 Ca. 170
After EN12163/12165.
Over ø 80mm after DIN1782
       
Top
Alloy
No. Casting methode Tensil strength 0,2 % Yield point Elongation Brinell hardness
EN 1706 and Alloy describtion Rm Rp0,2 A5 HB
    Min. N/mm2 Min. N/mm2 Min. % Min.
AC-Al Si7 Mg
EN AC-42000 F
Sand cast
140 80 2 50
  T6
Sand cast with heattreatment
220 180 1 75
  F
Chill cast
170 90 2,5 55
  T6
Chill cast with heattreatment
260 220 1 90
AC-Al Si10 Mg(a)
EN AC-43000 F
Sand cast
150 80 2 50
  T6
Sand cast with heattreatment
220 180 1 75
  F
Chill cast
180 90 2,5 55
    T6
Chill cast with heattreatment
260 220 1 90
AC-Al Si10 Mg(b)
EN AC-43100 F
Sand cast
150 80 2 50
  T6
Sand cast with heattreatment
220 180 1 75
  F
Chill cast
180 90 2,5 55
  T6
Chill cast with heattreatment
260 220 1 90
AC-Al Si9 Mg
EN AC-43300 T6
Sand cast with heattreatment
230 190 2 75
    T6
Chill cast with heattreatment
290 210 4 90
AC-Al Si12
EN AC-44200 F
Sand cast
150 70 5 50
  F
Chill cast
170 80 6 55
AC-Al Si12 Cu Ni Mg
EN AC-48000 T6
Chill cast
280 240 <1 100
AC-Al Mg5
EN AC-51300 F
Sand cast
160 90 3 55
  F
Chill cast
180 100 4 60
AC-Al Si8 Cu3
EN AC-46200 F
Sand cast
150 90 1 60
   
 F
Chill cast
170 100 1 75
AC-Al Zn5 Mg
EN AC-71000 T1
Sand cast with selfhardening
190 120 4 60
    T1
Chill cast with selfhardening
210 130 4 65
Top